We have adhesion strength problems on Tellurium Copper parts after Silver Plating. Of course, the parts are Pre silver plated. Brass Parts on the same rack are okay, the Tellurium Copper parts show blistering. Which would be the correct Pretreatment before silver plating or pre silver plating?